WOOD RESEARCH Volume 69, Number 2, 2024
VLADIMÍR IHNÁT, HENRICH LÜBKE, ALBERT RUSS, JOZEF BALBERČÁK, VLADIMÍR KUŇA, ANDREJ PAŽITNÝ, and ŠTEFAN BOHÁČEK

LIGNOCELLULOSIC LINERS BASED ON WOOD WOOL

Basic physical and mechanical properties of lignocellulosic liners up to 1.5 mm thick with a compact and non-crumbling surface based on wood wool and thermoplastic water based glues were determined. PVAc and starch glue with a high proportion of water content were used. The dry mat was pressed gradually under high pressure up to 28 MPa and a temperature of around 190°C with the release of steam. Tests according to the CEPI (Confederation of European Paper Industries) standards were adopted. Procedures for tensile strength according to ISO 1924-2 (2008), Burst strength according to ISO 2758 (2014), puncture according to ASTM D781-68 (1973), water absorption according to ISO 5637 (1989) and porosity according to TAPPI Test method T460 were applied

WOOD RESEARCH Volume 69, Number 1, 2024
VLADIMÍR IHNÁT, HENRICH LÜBKE, RASTISLAV ČEREŠŇA, JOZEF BALBERČÁK, VLADIMÍR KUŇA, ANDREJ PAŽITNÝ, and ŠTEFAN BOHÁČEK

THIN LIGNOCELLULOSIC LINERS BASED OF SPRUCE SHAVINGS

The article is devoted to determining the basic physical and mechanical properties of sheet materials up to 1.5 mm thick based on wood shavings and PVAc glue with a high proportion of water, pressed under high pressure up to 25 MPa and a temperature of around 190°C, so that the softening of lignin caused by the generated steam, allow to create a compact and non-crumbling surface. In order to characterize the physical-mechanical properties of the new wood-based sheet material with minimum thickness and characteristic elasticity, tests according to the CEPI (Confederation of European Paper Industries) standards were adopted. Procedures for tensile strength according to ISO 1924-2 (2008), Burst strength according to ISO 2758 (2014), puncture according to ASTM D781-68 (1973), water absorption according to ISO 5637 (1989) and porosity according to TAPPI Test method T460 were applied