Cadhesive bond performance of heat- treated fir wood (Abies borrissiregis)
The thermal treatment of wood leads to chemical, structural and natural changes in the wood components which can significantly affect the adhesive bond performance of the wood in various ways depending on the type of adhesive that is used. In the present research, fir wood (Abies borrissiregis) was undergone thermal treatment at 180°C, and 200°C for 3, 5 and 7 hours. Two different types of adhesives were used for the adhesive bond: polyurethane (PUR) and polyvinyl acetate PVAc. During all the wood treatment conditions, higher endurance in the bonding shear strength was noticed for the non-modified samples and the shearing strength by compression load was decreased while the thermal treatment was becoming more intense. Generally, while the PVAc bond shows better performance during the adhesion and higher modulus of rupture in comparison with the polyurethane PU after the thermal treatment of the wood.