Effect of tree diameter classes on the properties of persian oak (Quercus brantii Lindl.) wood
This study was conducted to investigate the properties of Persian oak (Quercus brantii Lindl.) wood, the most abundant tree species, harvested in the west and southwest regions of Iran. To the best our knowledge, there were no reported studies investigating the physical, chemical and biometrical features of Persian oak wood. For this purpose, 12 healthy trees in three diameter classes including 10-20, 20-30 and 30-40 cm were selected randomly and a disk was cut from each one at breast height. Results indicated that the highest basic densities are related to the diameter class 20-30cm (0.98 g.cm-3) and the lowest one at diameter class 10-20 cm (0.88 g.cm-3). The highest shrinkage was determined at oak wood samples from the diameter classes 10-20 cm (14.15%). Fiber length varied between 0.82 g.cm-3 (Dia. Class 10-20 cm, middle part) to 1.01 (Dia. Class 20-30 cm, bark). With increasing diameter, the cellulose content increased and the lignin content decreased while ash and extractive content was quite constant.