Study on preparation and properties of Anti-Ultraviolet Aging Wood-Plastic Composites
The degradable wood-plastic composites (WPC) were prepared by compression molding in this study. Polylactic acid (PLA), poly (butylene adipate-co-terephthalate) (PBAT) and salix powder were used as the main raw materials and nano-titanium dioxide (nano-TiO2) was used as anti-ultraviolet filler. The results show that when the addition amount of nano-TIO2 was 2%, the static bending strength and elastic modulus of WPC reach 41.88 MPa and 3730 MPa, respectively, which can meet the commercial application of WPC in building formwork. At this time, the composite material has a better effect of absorbing and reflecting ultraviolet light. The static bending strength, elastic modulus, tensile strength and impact strength of WPC were reduced by 68.3%, 61.5%, 51.9% and 57.4%, respectively. The mass loss rate and water absorption were 6.1% and 22.6%, respectively, that shows its good degradation performance. This study provides a low-cost and simple method for the design of anti-UV aging, high-performance and degradable WPC, which has broad application prospects in packaging, construction and other fields.