Dimensional stability of nano-SiO2/emulsified wax modified CuAz-treated wood after one year outdoor exposure test
Samples were vacuum-pressure treated with nano-SiO2 water solutions with BET specific surface area of 60,150, 200, 380 respectively, and then impregnated with copper azole (CuAz) preservatives or emulsified wax modified CuAz preservatives. The effects of emulsified wax and nano-SiO2 on the dimensional stability were investigated according to standard GB/T 1934 (2009) after one year outdoor exposure test. The results showed that the addition of nano-SiO2 or/and emulsified wax could reduce the water absorption rate of treated wood, and the best water repellent was observed in the samples treated with BET specific surface area of 60 m2.g-1. The addition of wax into nano-SiO2 modified wood was essential to improve the radial and tangential swelling and shrinkage stability of nano-SiO2 treated wood. The bigger BET specific surface area of nano-SiO2 would be adversely affected the dimensional stability of the treated wood.